| 厂家(产地)：日本帝人 | 牌号：E8715 BK | 销售方式：品牌经销 |
| 类型：标准料 | 加工级别：注塑级 | 特性级别：增强级 |
| 用途级别：通用级 |
物性表性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527 kg/cm?(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527-%拉伸模量 ASTM D638/ISO 5272400kg/cm?(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 5276%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527>50%弯曲模量(弯曲弹性率) ASTM D790/ISO 1782350kg/cm?(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 17893kg/cm?(MPa)[Lb/in2]洛氏硬度 ASTM D785 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 1183 成型收缩率 ASTM D9550.5~0.7%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133 g/10min220℃/10kgASTM D1238/ISO 1133 g/10min吸水率 23℃/24H ASTM D570/ISO 620.2%热性能热变形温度退火ASTM D648/ISO 75 ℃（℉）未退火ASTM D648/ISO 75 ℃（℉）维卡软化点 ASTM D1525/ISO R306146℃（℉）熔点 - ℃（℉）燃烧性（率） UL94 线性膨胀系数 ASTM D696/ISO 113590.7mm/mm.℃电气性能介电常数100HZASTM D150/IEC 602503 1MHZASTM D150/IEC 602503.1 介电损耗100HZASTM D150/IEC 60250 1MHZASTM D150/IEC 60250 体积电阻率 ASTM D257/IEC 60093>1×1013Ω.cm表面电阻率 ASTM D257/IEC 60093>1×1015Ω耐电弧性 ASTM D495/IEC 6011230 光学性能折射率 ASTM D542/ISO 4891.585 透光率 ASTM D1003/ISO 1346888%模糊系数（Haze） ISO 14782 %加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注 颜色 特性 用途 企业实景展示